Hifax TYC007P BLK very high melt flow, very high flexural modulus, UV-stabilized, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent balance of properties and processability. It is typically used for automotive bumper fascias.
Hifax TYC007P BLK
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (230 °C/2.16 kg) | 31 g/10 min |
| Density (23 °C) | 1.05 g/cm³ |
| Flexural Modulus (23 °C, 2 mm/min) | 2100 MPa |
| Tensile Modulus (23 °C, 50 mm/min, Chord) | 2000 MPa |
| Tensile Stress at Yield (23 °C, 50 mm/min) | 20 MPa |
| Notched Izod Impact Strength (23 °C) | 42 kJ/m² |
| Notched Izod Impact Strength (-30 °C) | 5 kJ/m² |
| Rockwell Hardness (R-Scale) | 63 |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 115 °C |
| Deflection Temperature Under Load (1.80 MPa, Unannealed) | 59 °C |
| Mold Shrinkage |
Technical Data Sheet
Technical Data SheetProcess
Injection Molding
Resin
Polypropylene Compounds
Applications
Automotive Parts, Bumpers, Exterior Automotive Applications
Prohibited Applications of Compounded Polyolefins:
The following applications and/or end uses are prohibited by LyondellBasell. LyondellBasell will not solicit the sale of, or knowingly supply, product for use in the following applications:
FDA Class III medical devices, European Class III medical devices, Health Canada Class IV Medical Devices, applications involving permanent implantation into the body & life-sustaining medical applications